材質
 用途
 化學成分
 力學能力
 線徑（mm）
 凈重(kg)
 閥芯直徑(mm)
 備注
 
ER304
 主要用于焊接18Cr-8Ni鋼
 C:0.064%

Mn:1.65%

Si:0.42%

Ni:8.33%

Cr:17.10%

 

 
 
 拉伸強度Mpa 1200
 0.08-0.45
 5/10/15/20
 100/270/300
 MIG:0.8-1.6

TIG:1.0-4.5
 
ER304L
 主要用于焊接17Cr-8Ni鋼
 C:0.028%

Mn:1.65%

Si:0.42%

Ni:8.33%

Cr:17.10%

 

 
 
 拉伸強度Mpa 1200
 0.08-4.5
 5/10/15/20
 100/270/300
 MIG:0.8-1.6

TIG:1.0-4.5
 
ER308
 主要用于焊接19Cr-9Ni鋼
 C:0.064%

Mn:1.65%

Si:0.42%

Ni:10.33%

Cr:20.10%
 拉伸強度Mpa 1200
 0.08-4.5
 5/10/15/20
 100/270/300
 MIG:0.8-1.6

TIG:1.0-4.5
 
ER308L
 主要用于焊接20Cr-9Ni鋼
 C:0.024%

Mn:1.65%

Si:0.42%

Ni:10.33%

Cr:20.10%

 

 
 
 拉伸強度Mpa 1200
 0.8-4.5
 5/12.5/15/20
 100/270/300
 MIG:0.8-1.6

TIG:1.0-4.5
 
ER309
 主要用于焊接20Cr-13Ni鋼
 C:0.064%

Mn:1.65%

Si:0.42%

Ni:14.33%

Cr:20.10%
 拉伸強度Mpa 1200
 0.08-4.5
 5/10/15/20
 100/270/300
 MIG:0.8-1.6

TIG:1.0-4.5
 
ER309L
 主要用于焊接20Cr-14Ni鋼
 C:0.024%

Mn:1.65%

Si:0.42%

Ni:14.33%

Cr:20.10%

 

 
 
 拉伸強度Mpa 1200
 0.08-4.5
 5/10/15/20
 100/270/300
 MIG:0.8-1.6

TIG:1.0-4.5
 
ER309Lsi
 主要用于焊接20Cr-14Ni鋼
 C:0.024%

Mn:1.65%

Si:1.02%

Ni:14.33%

Cr:20.10%
 拉伸強度Mpa1200
 0.08-4.5
 5/10/15/20
 100/270/300
 MIG:0.8-1.6

TIG:1.0-4.5
 
ER321
 主要用于焊接16Cr-7Ni鋼
 C:0.064%

Mn:1.65%

Si:0.42%

Ni:8.33%

Cr:17.10%Ti0.73
 拉伸強度Mpa 1200
 0.08-